Ruizhen Stainless Steel

410S

Alloy 410S is a low carbon, non–hardening modification of Alloy 410 the general purpose 12% chromium martensitic stainless steel. The low carbon and a small alloy addition minimize austenite formation at high temperatures which restricts the alloys ability to harden.

stainless steel 410S
USA
JP
DE
EUR
CN
ASTM
JIS
DIN
EN
GB
410S
SUS410S
X6Cr13
1.4000
06Cr13

Chemical Composition

The typical chemical composition is shown in the table below.

Grade
Standard
410S Chemical Composition
C
Si
Mn
Cr
Ni
P
S
Mo
Others
≤ %
≤ %
%
%
%
≤ %
≤ %
≤ %
%
410S
ASTM A240
0.08
1.0
1.0
11.5 - 13.5
0.6
0.04
0.015
-
-
1.4000
EN 10088-2
0.08
1.0
1.0
12.0 - 14.0
-
0.04
0.015
-
-
SUS410S
JIS G 4304 | JIS G 4305
0.08
1.0
1.0
11.5 - 13.5
0.6
0.04
0.03
-
-

Mechanical Properties

The mechanical properties are given in the table below.

Grade
Standard
410S Mechanical Properties
Tensile Strength
Yield Strength 0.2%
Elongation >%
Hardness
(MPa) ≥
(MPa) ≥
HRB ≤
HB ≤
410S
ASTM A240
415
205
19
89
183
1.4000
EN 10088-2
400-600
240
19
-
200
SUS410S
JIS G 4304 | JIS G 4305
410
205
20
88
183

Properties & Typical Applications

410S remains soft and ductile even when rapidly cooled from above the critical temperature. This non-hardening characteristic helps prevent cracking when the alloy is exposed to high temperatures or welded.Typical applications include petroleum refining, petrochemical processing,thermal processing , gate valves,press plates , heat exchangers,ore processing and mining machinery.